Mini-BRU/BIPS foil bearing development

The analysis revealed the failure agent to be a combination of poor teflon coating adhesion, a decrease in bearing sway space and, possibly, lack of flushing flow through the bearing. A change in Teflon coating vendors provided substantially improved coating quality and surface finish. The sway space was increased and the cooling bleed flow was adjusted to flush the bearing. These changes were included in a test conducted in the WHL from 6 April to 22 May 1978 which resulted in the completion of 1006.9 hours of operation at temperature and load. Post-test inspection revealed the bearings to be in excellent condition and capable of completing a much longer test.