Phase Two of the Array Automated Assembly Task for the Low Cost Solar Array Project

Various top contact metal systems were studied. Only Ti Pd Cu approaches baseline (Ti Pd Ag) quality, but this system shows a lack of long term stability. Aluminum back surface field structures were fabricated and thicknesses of p superscript + material of up to 7.0 microns were achieved with open circuit voltages of 0.59V. A general purpose ultrasonic welder was purchased and tests using various metal foils are under way. During fabrication of the demonstration module, several cells became cracked. Due to redundancy of interconnections, the module was not open circuited but the efficiency was reduced to 8.8%. The broken cell was interconnected with a strap across the back and the efficiency was increased to 11.5%. A cost analysis was made and the results indicate a selling price of $0.56/watt peak (in 1986 with 1975 dollars).