Large Area Silicon Sheet by EFG

Influences on ribbon quality which might be caused by various materials of construction which are used in the growth furnace were assessed. At the present level of ribbon quality, which has produced 8.5% to 9.5% efficient solar cells, no particular influence of any furnace part was detected. The experiments led to the suspicion that the general environment and the somewhat unoptimized materials handling procedures might be responsible for the current variations in ribbon quality and that, therefore, continuous work with this furnace under rather more stringent environmental conditions and operating procedures could perhaps improve materials quality to some extent. The work on the multiple furnace was continued with two multiple growth runs being performed. In these runs, the melt replenishment system performed poorly and extensive modifications to it were designed to make reliable melt feeding for five ribbon growth possible. Additional characterization techniques for wide ribbons, stress measurements, and growth dynamics experiments are reported.