Modules of rupture and oxidation resistance of S12.55Al0.6O0.72N3.52 sialon

A Sialon of formula Si2.55Al0.6O0.72N3.52 was made from ball-milled alpha-Si3N4, AIN, and SiO2 by sintering the powder compacts at 1760 C for 4 hours in stagnant nitrogen. This Sialon had an average modulus of rupture ranging from 404 megapascals (58.6 ksi) at room temperature to 254 megapascals (36.8 ksi) at 1400 C. Oxidation tests at 1400 C in air showed it to have a parabolic oxidation rate constant less than or equal to 2.8x10 to the -10th power sq g/cm4 hr, which is smaller than that of any other Si3N4-base ceramic reported in the literature.