Analyses of moisture in polymers and composites

A suitable method for the direct measurement of moisture concentrations after humidity/thermal exposure on state of the art epoxy and polyimide resins and their graphite and glass fiber reinforcements was investigated. Methods for the determination of moisture concentration profiles, moisture diffusion modeling and moisture induced chemical changes were examined. Carefully fabricated, precharacterized epoxy and polyimide neat resins and their AS graphite and S glass reinforced composites were exposed to humid conditions using heavy water (D20), at ambient and elevated temperatures. These specimens were fixtured to theoretically limit the D20 permeation to a unidirectional penetration axis. The analytical techniques evaluated were: (1) laser pyrolysis gas chromatography mass spectrometry; (2) solids probe mass spectrometry; (3) laser pyrolysis conventional infrared spectroscopy; and (4) infrared imaging thermovision. The most reproducible and sensitive technique was solids probe mass spectrometry. The fabricated exposed specimens were analyzed for D20 profiling after humidity/thermal conditioning at three exposure time durations.