Thermal cycling graphite-polyimide

The effects of repetitive thermal cycling on the temperature-thermal deformation relation of graphite-polyimide were determined. The bending and axial strains, measured with strain gages, of unsymmetric 0 deg sub 2/90 deg sub 2 and 0 deg sub 4/90 deg sub 4 laminates were used as an indication of thermal deformation. The strains were measured as a function of temperature and two temperature ranges were used, room temperature to 180 C and room temperature to 315 C. Five cycles were run in each temperature range and the cycling was done in quasistatic fashion. The response of a flat 0 deg sub 8 laminate was measured as were the effects of repetitive cycling on the strain gages themselves. A piece-wise linear theory, based on classical lamination theory and using the variation of mechanical and thermal expansion properties with temperature, was compared with the experimental results. The correlation between theoretical predictions and experimental results for the thinner laminate was poor.