Mass loss of a TEOS-coated, reinforced carbon-carbon composite subjected to a simulted shuttle entry environment

Coated, reinforced carbon-carbon (RCC) is used for the leading edges of the space shuttle. The mass loss characteristics of RCC specimens coated with tetraethyl orthosilicate (TEOS) were determine for conditions which simulated the environment expected at the lug attachment area of the leading edge. Mission simulation included simultaneous application of load, temperature, and oxygen partial pressure. Maximum specimen temperature was 900 K (1160 F). Specimens were exposed for up to 80 simulated missions. Stress levels up to 6.8 MPa (980 psi) did not significantly affect the mass loss characteristics of the TEOS-coated RCC material. Mass loss was correlated with the bulk density of the specimens.