Fracture toughness of silicon

The paper presents a study to determine the fracture toughness and to characterize fracture modes of silicon as a function of the orientation of single-crystal and polycrystalline material. It is shown that bar specimens cracked by Knoop microhardness indentation and tested to fracture under four-point bending at room temperature were used to determine the fracture toughness values. It is found that the lowest fracture toughness value of single crystal silicon was 0.82 MN/m to the 3/2 in the 111 plane type orientation, although the difference in values in the 111, 110, and 100 planes was small.