Insulators for Pb(1-x)Sn(x)Te

Thin films of LaF3 were e-gun and thermally deposited on several substrates. The e-gun deposited films are fluorine deficient, have high ionic conductivities that persist to 77 K, and high effective dielectric constants. The thermally deposited material tends to be closer to stoichiometric, and have higher effective breakdown field strengths. Thermally deposited LaF3 films with resistivities in excess of 10 to the 12th power ohms - cm were deposited on metal coated glass substrates. The LaF3 films were shown to adhere well to PbSnTe, surviving repeated cycles between room temperature and 77 K. The LaF3 films on GaAs were also studied.