Flaw growth of 6Al-4V STA titanium in nitrogen tetroxide with low nitric oxide content

The sustained load flow growth characteristics of surface flowed 6Al-4V STA titanium specimens were determined when exposed to nitrogen tetroxide N2O4 having nitric oxide (NO) concentrations of 0.06 to 0.30%. Test temperatures ranged from 70 to 150 F. It was observed that the threshold stress intensity for the titanium decreased abruptly below on NO concentration of 0.18% and also decreased as the temperature increased. The threshold stress intensity was determined to be greater than or equal to 60% of the critical stress intensity for NO concentrations of 0.18 to 0.30% and temperatures of 90 and 120 F. Sustained load tests conducted in N2O4 vapor with a 0.30% NO concentration at 120 F indicated the threshold to be also greater than or equal to 60% of critical.