Study of the effects of gaseous environmental on the hot corrosion of superalloy materials

Studies have been conducted to examine the effect of low concentrations of NaCl(g) on the high temperature oxidation behavior of complex superalloys and potential coating formulations modified by silicon and reactive element (i.e., yttrium and hafnium) additions. Depending on alloy composition, a variety of effects were thermogravimetrically produced. Aluminum free alloys such as MAR-M509 and Hastelloy X with molybdenum and tungsten in solid solution showed accelerated (or breakaway) kinetics similar to that observed for Ni-Cr alloys. For IN-792, an alloy high in chromium and low in aluminum, molybdenum and tungsten present in solid solution does not adversely affect oxidation kinetics in the presence of NaCl(g). On the other hand, nickel-base alloys high in aluminum and molybdenum are catastrophically attacked by NaCl-bearing atmospheres. Silicon additions were, in general, observed to slightly improve the oxidation resistance of Ni, Ni-40Cr and CoCrAlY compositions in NaCl(g)-bearing atmospheres. To the degree that processes responsible for Al2O3 whisker formation deleteriously affect protective scale adherence, the addition of yttrium or hafnium can inhibit such whisker growth.