On failure modes in finite width angle ply laminates

The results of a failure analysis of finite width (+ or - theta)s T300/5208 graphite-epoxy laminates subjected to thermal curing loads and applied tensile strain are presented. Stress distributions obtained from linear elastic and linear thermoelastic finite element stress analyses are used in conjunction with the tensor polynomial failure criterion to predict the mode and location of first failure in laminates with fiber angles ranging from five to seventy-five degrees. It is shown that the mode of failure is predominantly interlaminar shear for small fiber angles, shifts to combined interlaminar normal, in-plane shear and in-plane normal for intermediate angles, and is primarily transverse tension for large fiber angles. The location of initial failure shifts from the (+ or - theta)s interface for small fiber angles to the midplane for large fiber angles.