Large area silicon sheet by EFG

Progress was made in improving ribbon flatness and reducing stress, and in raising cell performance for 10 cm wide ribbon grown in single cartridge EFG furnaces. Optimization of growth conditions resulted in improved ribbon thickness uniformity at a thickness of 200 micron, grown at 4 cm/minute, and growth at this target speed is routinely achieved over periods of the order of one hour or more. With the improved ribbon flatness, fabrication of large area (50 cm2) cells is now possible, and 10 to 11% efficiencies were demonstrated on ribbon grown at 3.5 to 4 cm/minute. Factors limiting performance of the existing multiple ribbon furnace were identified, and growth system improvements implemented to help raise throughput rates and the time percentage of simultaneous three-ribbon growth. However, it is evident that major redesign of this furnace would be needed to overcome shortfalls in its ability to achieve the Technical Features Demonstration goals of 1980. It was decided to start construction of a new multiple ribbon furnace and to incorporate the desired improvements into its design. The construction of this furnace is completed.