Method for forming pyrrone molding powders and products of said method

The formation of pyrrone resins of the ladder or semiladder structure is described. The technique involves initial formation of fully cyclized prepolymers having an average degree of polymerization of about 1.5, one with acidic terminal groups, another with amine terminal groups. Thereafter the prepolymers are intimately admixed on a 1:1 stoichiometric basis. The resulting powder mixture is molded at elevated pressures and temperatures to form a fully cyclized resin.