FSA field test report, 1980 - 1982

Photovoltaic modules made of new and developing materials were tested in a continuing study of weatherability, compatibility, and corrosion protection. Over a two-year period, 365 two-cell submodules have been exposed for various intervals at three outdoor sites in Southern California or subjected to laboratory acceptance tests. Results to date show little loss of maximum power output, except in two types of modules. In the first of these, failure is due to cell fracture from the stresses that arise as water is regained from the surrounding air by a hardboard substrate, which shrank as it dried during its encapsulation in plastic film at 150 C in vacuo. In the second, the glass superstrate is sensitive to cracking, which also damages the cells electrostatically bonded to it; inadequate bonding of interconnects to the cells is also a problem in these modules. In a third type of module, a polyurethane pottant has begun to yellow, though as yet without significant effect on maximum power output.