Materials investigation of STS-3 parachute failure

Main parachute, No. 2 of SRB A-12 on STS-3, sustained damage during deployment or initial inflation that resulted in its collapse and failure to sustain load. During an investigation of the materials from this parachute, optical and scanning electron microscope analyses were conducted. This examination identified stains and abrasions on vent lines that appear to have been a result of friction contact with its flotation bag lanyard. Mechanical testing of the vent band indicated a reduction in strength of 37 percent obviously due to structural overload, heat, and ocean water exposure. It is concluded from this and other available data that entanglement of parachutes No. 1 and No. 2 during deployment caused adequate structural damage to main parachute No. 2 to render it unable to carry load.