Tribological measurements on a Charnley-type artificial hip joint

A total hip simulator was used to determine the friction and wear properties of Charnley-type (316L stainless steel balls and sterile ultrahigh molecular weight polyethylene cups) hip prostheses. Three different sets of specimens were tested to 395,000, 101,500 and 233,000 walking cycles, respectively. All tests were run unlubricated, at ambient conditions (22 to 26 C, 30 to 50 percent relative humidity), at 30 walking cycles per minute, under a dynamic load simulating walking. Polyethylene cup wear rates ranged from 1.4 to 39 ten billions cu m which corresponds to dimensional losses of 4.0 to 11 microns per year. Although these wear rates are lower than those obtained from other hip simulators and from in vivo X-ray measurements, they are comparable when taking run-in and plastic deformation into account. Maximum tangential friction forces ranged from 93 to 129 N under variable load (267 to 3090 N range) and from 93 to 143 N under a static load of 3090 N. A portion of one test 250,000 walking cycles) run under dry air ( 1 percent relative humidity) yielded a wear rate almost 6 times greater than that obtained under wet air ( 70 percent relative humidity) conditions.