Surface topography-connections between lubrication and failure initiation

The characteristics of the initial surface topography is intimately connected to the machining process by which it is produced. Both processes create a near surface region of residual stresses, microstructure and hardness that is different from the bulk. The material properties in this rather undefined region can significantly influence the mode of failure, such as wear, scuffing or fatigue, as well as the degree of failure resistance for a given material. Under full film elastohydrodynamic (EHD) conditions, where shear is accomodated within a relatively thick lubricant film, the normal and shear stresses are distributed uniformly over the near surface region, and the surface topography has little influence on the lubrication or failure process. Under more typical conditions where surface roughness and lubricant film thickness are of the same order of magnitude, the surface topography not only emerges as an important parameter in failure initiation, but it also becomes intimately involved in the lubrication process itself.