LEO atomic oxygen effects on spacecraft materials: STS-5 results

Effects of low Earth orbit (LEO) atomic oxygen were measured on a variety of spacecraft materials which obtained exposure on STS-5. Material degradation dependency on temperature was found in one material. Of the five paints flown, only S13GLO was unaffected. Generally, the glossy paints became Lambertian and the diffuse coatings improved. Scanning electron microscope examinations indicated removal of urethane and epoxy paint binder materials. Reaction products were evident on the surfaces of Z302 paint and Mylar. Thin films showed thickness losses ranging from negligible loss in Teflon to considerable loss in Mylar and Kapton. Glossy films such as black Kapton and white Tedlar became diffused. Kevlar 29 rope lost tensile strength and silver solar cell interconnect material oxidized. Oxidation on the backside of an elevated specimen indicated that reflections of oxygen atoms were occurring and that reflecting surfaces, probably Kapton, were not fully accommodating the incident atoms.