Thermal aging of graphite/polyimide composites

Celion 6000/PMR-15, Celion 6000/LARC-160, and Celion 6000/RK-99 graphite/polyimides were aged in circulating air ovens at temperatures of 202, 232, 260, and 288 C for various times, up to 15,000 h. Three unidirectional specimens were studied: short-beam-shear (SBS), flexure, and 153-mm square panels. The interior region of the square panels exhibited little or no property degradation. Based on the individually aged SBS specimen results, the relative thermal-oxidative stability from highest to lowest is as follows: PMR-15, LARC-160, RK-99, Celion 6000/PMR-15 and Celion 6000/LARC-160 laminates retained at least 80 percent of their initial flexural strengths for the duration of aging at each temperature. Celion 6000/RK-99 laminates exhibited a 20 to 50 percent loss of flexural strength at all aging temperatures. All three graphite/polyimide laminate materials degraded preferentially at the specimen edge perpendicular to the fibers.