Investigation of the effects of NaOH dopant level on the physical and mechanical properties of carbon/phenolic composite material

The near-catastrophic erosion of the STS-8A solid rocket booster nozzle was the instigating factor in the recent, and on-going, intensive investigation of carbon/phenolic composite materials. Much of this effort has been focused on the effect of sodium contamination on the carbon fibers. It is known that sodium acts as a catalyst in the oxidation of the fibers at elevated temperatures. A study was undertaken to determine what changes were caused by variation in sodium content. Investigations were conducted in three areas: (1) phenolic resin; (2) carbon/phenolic prepreg; and (3) cured laminates. Due to the exploratory nature of the studies, a variety of tests in addition to those normally run in production facilities were considered. The experimental methodologies and results of these experiments are discussed, and recommendations for improving techniques and extending the research program are presented.