Stress and efficiency studies

Optical and electrical characterization of defects has been started in EFG ribbon grown in a system that will be used to test the stress model. Temperature and stress field modeling aimed at defining low stress growth configuration is also in progress, and results will be used to guide development of the experimental system. The baseline defect configuration for ribbon grown at speeds of approx. 1 cm/min consists of dislocation densities of the order of 10 to the 5th power to 10 to the 6th power/sq cm, as well as saucer type etch pits and line defects. All these defects are inhomogeneously distributed. EBIC measurements indicate that diffusion lengths are in the range 20 to 60 microns, and significant spatial inhomogeneities occur through the ribbon thickness. Growth speed changes in the range 0.7-1.0 cm/min do not produce significant variations in ribbon defect configurations.