The aging correlation (RH + t): Relative humidity (%) + temperature (deg C)

An aging correlation between corrosion lifetime, and relative humidity RH (%) and temperature t (C) has been reported in the literature. This aging correlation is a semi-log plot of corrosion lifetime on the log scale versus the interesting summation term RH(%) + t(C) on the linear scale. This empirical correlation was derived from observation of experimental data trends and has been referred to as an experimental law. Using electrical resistivity data of polyvinyl butyral (PVB) measured as a function of relative humidity and temperature, it was found that the electrical resistivity could be expressed as a function of the term RH(%) t(C). Thus, if corrosion is related to leakage current through an organic insulator, which, in turn, is a function of RH and t, then some partial theoretical validity for the correlation is indicated. This article describes the derivation of the term RH(%) t(C) from PVB electrical resistivity data.