Fracture surface analysis in composite and titanium bonding

Carbon fibers were obtained from several manufacturers. Surface treatments were performed on these fibers by anodization. The surfaces of these fibers were analyzed by X-ray photoelectron spectroscopy and wetting force measurement. The breaking strength of these fibers was measured at 2.5 cm length. It was seen that the surface treatments reduces the strength of the fibers. It was also seen that the Hercules fibers had a higher breaking strength than the Union Carbide fibers. Fiber critical length measurements showed no difference in critical lengths between AS-4 and AU-4 fibers embedded in polysulfone. However, the fiber lengths were much shorter for the surface treated fibers. This effect could be related to increased adhesion between fiber and matrix, or it could be due to the lower breaking strength of the surface treated fiber.