High-temperature gaseous oxygen/hydrogen thrusters for space station

Efforts to determine the critical technologies necessary for the development of a high-temperature GO2/GH2 thruster are reviewed, for space station applications. Two types of thrust chambers are evaluated: one operable at high temperature and the other incorporating regenerative cooling. The high temperature chamber made of rhenium requires minimum cooling of the chamber wall, however, an oxidation barrier should be incorporated to prevent the rhenium thruster from readily oxidizing. The use of rhenium brought about a lower cost, lower weight, and simplicity of fabrication. The igniter-injector, the chamber, the test facility, and the test program are discussed. It is found that an obtained flow split of 58/42 increased the thruster performance from 3893 N-s/Kg to 4030 N-s/Kg for the same chamber pressure and overall mixture ratio. An increase in performance is also observed when the core mixture ratio is lowered. The thruster was tested for 1.9 hrs with no well degradation.