InGaAs/InAlAs hot-electron transistor

Using InGaAs for the base and InAlAs for the emitter and collector barriers, the first hot-electron transistor in this material system is fabricated. It is shown that 1.6 percent of the injected hot electrons can be transported ballistically through a 0.3 micron thick In(0.53)Ga(0.47)As plus 800-A-thick InAlAs barrier layer at 77 K giving rise to an average mean free path of 920 A. An energy spread of 130 MeV was observed for the ballistic electrons injected at about 700 MeV above the thermal equilibrium conditions. The value of collector barrier heights measured are in reasonable agreement with those deduced independently from thermionic emission studies in InGaAs gate, InAlAs/InGaAs capacitor structures.