Reliability and engineering sciences area. Materials research: Single junction thin film

A test bench was designed and fabricated for the purpose of improving control of hot-spot test accuracy. Electrochemical corrosion research focused on corrosion mechanisms to which both crystalline and a-Si modules may be subjected in central station applications. A variety of cells and several designs were subjected to accelerated stress tests. Humiditiy degradation rates were determined and key electrochemical failure mechanisms were identified. Software was developed for the prediction of power loss resulting from open circuits in an array field of a-Si modules. Failure analysis was continued on the four ARCO Solar Genesis modules. The interactions of water on the silicon module was examined. An autocatalytic photooxidation model was proposed. The reliability and durability of bonding materials and electrical insulation were also studied.