Radiation and temperature effects in gallium arsenide, indium phosphide and silicon solar cells

The effects of radiation on performance are determined for both n(+)p and p(+)n GaAs and InP cells and for silicon n(+)p cells. It is found that the radiation resistance of InP is greater than that of both GaAs and Si under 1 MeV electron irradiation. For silicon, the observed decreased radiation resistance with decreased resistivity is attributed to the presence of a radiation induced boron-oxygen defect. Comparison of radiation damage in both p(+)n and n(+)p GaAs cells yields a decreased radiation resistance for the n(+)p cell attributable to increased series resistance, decreased shunt resistance, and relatively greater losses in the cell's p-region. For InP, the n(+)p configuration is found to have greater radiation resistance than the p(+)n cell. The increased loss in this latter cell is attributed to losses in the cell's emitter region. Temperature dependency results are interpreted using a theoretical relation for dVoc/cT which predicts that increased Voc should results in decreased numerical values for dPm/dT. The predicted correlation is observed for GaAs but not for InP a result which is attributed to variations in cell processing.