Garnet melt viscosity, surface tension and drainage

Good surface morphology and layer uniformity of LPE-grown Bi YIG films are favored by fast melt removal after growth. Three flux modifying oxides: MoO3, V2O3, and WO3 are compared with respect to their effect on viscosity, surface tension and melt drainage. All three oxides increased the viscosities of Bi-garnet melts, but the viscosities and drainage times of V2O3 and MoO3 modified melts were smaller than those of WO3 modified melts. The liquid-gas surface tension was found to be temperature independent. The drainage process was strongly temperature dependent, 40 to 60 kcal/mol, whereas the viscosities of melts had activation energies of 11 to 16 kcal/mol. Contact angles of 16 + or - 2 deg were measured on frozen melt drops.