Partial analysis of experiment LDEF A-0114

Due to delays in manifesting the return of the Long Duration Exposure Facility from space, attention was concentrated on extracting the maximum information from the EIOM-2 (oxygen interaction with materials experiment) flown on STS-8 in September 1983. An analysis was made of the optical surfaces exposed during that flight and an assessment made of the effect of the 5 eV atomic oxygen upon their physical and chemical properties. The surfaces studied were of two types: high-purity thin films sputtered or evaporated onto 2.54-cm diam lambda/20 fused silica optical flats, and highly polished bulk samples. Rapid etching of carbon and carbonaceous surfaces was observed with polycarbonate CR-39 showing the largest etch of any substrate flown and measured. Of the metals tested, only osmium and silver showed large effects, the former being heavily etched and the later forming a very thick layer of oxide. The first measurable effects on iridium, aluminum, nickel, tungsten and niobium thin films are reported.