Fractography of composite delamination

Studies were made of the fractography of mode 2 delamination and the impact damage of carbon fiber reinforced polymer composites. Laminates fractured under mode 2 loading were potted in a clear epoxy polymer, sectioned and polished and examined using transmission and reflection light microscopy. There were only occasional fibers bridging the mode 2 cracks. These cracks were not always visible probably because the crack opening displacement was too small as to be resolved using light microscopy. A study was made of the effect of repetitive impacts on laminates of AS4/3501-6 and IM6/3501-6. Plots of cumulative impact energy vs cumulative absorbed energy exhibited a sharp change in slope which corresponded to the damage area reaching the edges of the specimen. The initial slope was highly reproducible for both composite materials. On the other hand, the intersection point between the two slopes, where the damage area reaches the specimen edges, was highly variable between specimens. This variability is tentatively ascribed to differences in laminate quality.