Fractographic and microstructural evaluation of 3500-hour durability specimens

Long term durability testing of candidate ceramic materials for advanced gas turbine applications was performed. Specimens of the materials were exposed to combustion atmospheres under temperature cyclic conditions for times up to 3500 hours and at peak temperatures of 1200 and 1370 C. The specimen strengths after exposure were measured at room temperature and at 1200 C. In addition, a number of physical measurements were taken; however, no microstructural examination of the specimens was performed. Materials examined include: sintered alpha silicon carbide, sintered silicon nitride, and reaction bonded silicon nitride. Sample preparation techniques were developed to provide high quality thin-section specimens which can be examined by transmitted light or thinned using an ion mill for subsequent transmission electron microscopic examination. Specimen preparation techniques and the results of optical and electron microscopic examination of the reaction interfaces of the selected specimens are presented.