Damage growth in composite laminates with interleaves

The influence of interleaves on the fracture behavior of laminated composites is investigated. The geometry of the composite consists of a cracked layer, bonded between two half-planes, which is separated by thin, low modulus, interleaves. The interleaves are modeled as uncoupled tension and shear springs. A stress analysis is carried out for a crack which may grow up to and spread along the interface. Integral transform techniques are used to develop the solution in terms of singular integral equations. An asymptotic analysis reveals logarithmic singularities in the critical stresses for the case of a broken layer. The equations are solved numerically and the effect of damage on critical stresses is studied. Initial results indicate that the interleaf gives a significant reduction in stresses in the adjacent regions and, if properly selected, should result in a more damage tolerant laminate.