Dispersion strengthened NiAl alloys produced by rapid solidification processing

Initial experimental results are presented concerning the relationship between microstructure and properties in rapidly solidified NiAl alloys whose melting point is of the order of 1900 K. When the dispersoid content of NiAl alloys is increased, the dispersoids begin to populate the grain boundaries, rendering them weak, so that failure must propagate intergranularly. It is concluded that NiAl alloys' strength can be significantly increased through dispersoid additions without sacrifice of high temperature ductility.