Microscopic deformation in a heated unidirectional graphite-epoxy composite

Both in-plane and out-of-plane displacements were determined in patches of the toughened 1962-ERLX epoxy bounded by three closely packed high-modulus P75S graphite fibers. The P75S/1962-ERLX composite was unidirectional, with an average fiber volume of 60 percent. On heating to 44 C from room temperature, the epoxy confined between clusters of three fibers sank in a trough beneath the plane of the fiber ends by 50-120 nm. When the maximum temperature achieved in the prior thermal cycles exceeded 100 C the depth of the trough increased. However, when cycles exceeding 100 C were followed by thermal cycles of decreasing amplitude, chosen to reduce interfacial stress relaxation, the depth of the trough decreased. The results illustrate the feasibility of deducing quantitative data on local deformation from high-resolution strain measurements on cut surfaces.