Millimeter wave surface resistance of RBa2Cu3O(7-delta) (R=Y,Eu,Dy,Sm,Er) superconductors

The measurements are reported of the millimeter wave surface resistance R(sub s) at 58.6 GHz of bulk samples of RBa2Cu3O(7-delta) (R = Y,Eu,Dy,Sm,Er) and of YBa2Cu3O(7-delta) superconducting films, in the temperature range from 20 to 300 K. The bulk samples were prepared by cold pressing the powders of RBa2Cu3O(7-delta) into one in. disks. The powders were prepared by several sinterings in one atmosphere of oxygen at 925 C, with grindings between sinterings, to obtain the superconducting phase. The thin films were deposited on SrTiO3 and LaGaO3 substrates by pulsed laser ablation. Each sample was measured by replacing the end wall of a gold-plated Te sub 013 circular mode copper cavity with the sample and determining the cavity quality factor . From the difference in the Q-factor of the cavity, with and without the sample, the R(sub s) of the sample was determined.