Analysis of Pt/SnO(sub x) during catalysis of CO oxidation

Temperature-programmed reduction using 6kPaH2 suggests that a sample consisting of 3 percent Pt supported directly on SnO2 is, under conditions of catalysis of CO oxidation used here, best represented as 3 percent Pt/SnO sub x, since the support is likely to partially reduced, probably in the vicinity of the metal/oxide interface. Catalytic measurements at 421 to 424 K show that this 3 percent Pt/SnO sub x is significantly more active per unit area of Pt than 6 percent Pt/SiO2 in catalyzing the oxidation of CO. In situ micro-FTIR reveals that while the latter has predominantly linearly bound CO on the surface under reaction conditions, the Pt/SnO sub x also has a species absorbing at 2168 cm(exp -1) which may be CO upon Pt in a positive oxidation state or weakly chemisorbed CO on zero-valent Pt. This may be directly involved in the low temperature oxidation of CO on the Pt/SnO sub x, since being weakly held the activation energy for its surface diffusion to the metal/oxide interface will be low; such mobile species could allow the high rates of surface transport and an increase in the fraction of the surface over which the CO oxidation occurs. FTIR also reveals carbonate-type species on the P/SnO sub c surface.