Superconductivity in the Sn-Ba-Sr-Y-Cu-O system

Since Bednorz and Muller discovered high-T(sub c) superconductivity in the La-Ba-Cu-O compound, several families of superconducting oxides have been synthesized. Here, researchers report the results of search for superconductivity in the compounds based on tin, which has a lone electron pair like Bi, Tl, Pb. The following compounds were synthesized: Sn1Ba1Sr1Cu3Ox, Sn1Ba1Ca1Cu3Ox, Sn1Ba1Mg1Cu3Ox, Sn1Sr1Ca1Cu3Ox, Sn1Sr1Mg1Cu3Ox, Sn1Ca1Mg1Cu3Ox. The initial components were oxides and carbonates of the appropriate elements. Standard firing-grinding procedure was used. Final heating was carried out at 960 C during 12 hours. Then the samples were cooled inside the furnace. All the synthesis cycles were carried out in air atmosphere. Among the synthesized compounds only Sn1Ba1Sr1Cu3Ox showed remarkable conductivity. Other compounds were practically dielectrics. Presence of a possible superconductivity in Sn1Ba1Sr1Cu3Ox was defined by using the Meissner effect. At low temperature a deviation from paramagnetic behavior is observed. The hysteresis loops obtained at lower temperatures undoubtly testify to the presence of a superconductive phase in the sample. However, the part of the superconductive phase in the Sn1Ba1Sr1Cu3Ox ceramic turned out to be small, less than 2 percent, which agrees with the estimation from magnetic data. In order to increase the content of the superconductive phase two-valent cations Ba, Sr were partially substituted by univalent (K) and three-valent ones (Y).