Polyimide matrix composites - Polyimidesulfone/LARC-TPI (1:1) blend

Polyimide matrix composites were fabricated from unidirectional unsized AS-4 carbon fiber and a doped 1:1 blend of two polyimides: PISO2 and LARC-TPI. To enhance melt flow properties, the molecular weight of the PISO2 was controlled by end-capping with phthalic anhydride and addition of 5 percent by weight p-phenylenediamine-phthalic anhydride bisamic acid dopant. Prepreg was drum-wound using a diglyme slurry comprised of the soluble polyamideacid of PISO2, the soluble bisamideacid of the dopant, and the insoluble imidized LARC-TPI powder. Melt flow studies with a rotary rheometer and parallel plate plastometer on neat resin and prepreg helped develop an optimum cure cycle. Composite mechanical properties at room and elevated temperatures, dry and moisture-saturated, were evaluated, including short beam shear strength and flexure, tensile, shear, and compression properties. Two 18 x 24-inch skin-stringer panels were fabricated, one of which was tested in compression to failure.