Directional solidification of Pb-Sn eutectic with vibration

Pb-Sn eutectic alloy was directionally solidified at 1.4 to 3.2 cm/hr with forced convection induced by axial vibration of the growth ampoule with a frequency of 10 to 40 Hz and an amplitude of 0.5 to 1.0 mm. To determine the exact growth rate, an interface demarcation technique was applied. The lamellar spacing was increased 10 to 40 percent in ingots solidified with vibration compared to those solidified without vibration. The average intensity of convection in the melt under axial vibration of the ampoule was estimated by comparing the experimental results with a theoretical model.