Effect of Li level, artificial aging, and TiB2 reinforcement on the fracture toughness of Weldalite (tm) 049-type alloys

Plane strain fracture toughness (K sub IC) was evaluated for Weldalite (tm) 049 with and without TiB2 reinforcement. For the nonreinforced variant, changes in toughness were measured for various aging conditions and lithium levels. Toughness testing was carried out on fatigue precracked compact tension (CT) specimens at 24 C, as per ASTM standard E-399. Toughness was measured as a function of aging time at 160 C for the two Weldalite 049(1.3) heats. The composition of these heats differed only in that 0.03 wt pct. Ti was added to one as an additional grain refiner. Both heats showed a decrease in toughness with increasing aging time, although toughness values for one were significantly higher than for the other. This greater toughness may be due to a subtle change in the grain size resulting for the presence of Ti or, alternatively, to differences in texture or substructure formed during extrusion.