Effect of Li level, artificial aging, and TiB2 reinforcement on the modulus of Weldalite (tm) 049

The dynamic Young's Modulus (E) was determined for (1) alloys 049(1.3)(heat 072), (2) 049(1.9), and (3) 049(1.3) TiB2 in the T3 temper and after aging at 160 C were made on a single 0.953 cm (0.375 in) cube to reduce scatter from microstructural inhomogeneities. Both shear and transverse wave velocities were measured for the L, LT, and ST directions by a pulse echo technique. These velocities were then used to calculate modulus. The change is shown in E with aging time at 160 C (320 F) for the three alloys. It is clear from the plots that aging has a minor, but measurable, influence on the E of alloys 049(1.3) and 049(1.9): E decreases by -2.5 pct. for 2 and 3 during the initial stages of artificial aging. This decrease in E generally follows the strength reversion. On further aging beyond the reversion well, E increases and then decreases again as the alloy overage. The slightly higher modulus in the T8 than in the T3 temper is consistent with the presence of the high modulus T sub 1 phase in the T8 temper. A similar change in E was observed on aging for the TiB2 reinforced variant that also follows the aging curve.