Polyimides with pendent ethynyl groups

Several new polyimides containing pendent ethynyl groups were prepared and characterized. The new polyimides were prepared from the following novel ethynyl containing diamines; 1,1-bis(p aminophenyl)-1-(p ethynylphenyl) 2,2,2-trifluoroethane, and 1,1-bis(p aminophenyl)-1-(p phenylethynylphenyl)-2,2,2 trifluoroethane, and 1,1-bis(p aminophenyl)-1-(p hexynylphenyl)-2,2,2 trifluoroethane by reacting with either 3,3',4,4' benzophenone tetracarboxylic dianhydride or 2,2-bis(3,4 dicarboxyphenyl) hexafluoropropane dianhydride (6FDA). Inherent viscosities for the polymers ranged from 0.26 to 0.94 dL/g. Three copolymers prepared by reacting 10 mole pct. of one of the ethynyl containing diamines and 90 mole pct. of 2,2-bis-(4-(4 aminophenoxy)phenyl) hexafluoropropane with 6FDA were also prepared and characterized. Inherent viscosities for these copolymers ranged from 1.08 to 1.54 dL/g. Original polyimide glass transition temperatures were approx. 265 C while curing at 300 to 350 C for 1 hr in air increased the Tgs by approx. 10 C. Film properties and thermal stability were also measured for these copolyimides.