Preparation and characteristics of superconducting cuprate thin films: Nd(2-x)Ce(x)CuO4 and substrated Bi-system

Characteristics of the electron-doped-type Nd(sub 2-x)Ce(sub x)CuO4 system and substituted Bi-system were studied using the high quality thin film samples grown by rf magnetron sputtering and/or subsequent heat treatment. The Nd(sub 2-x)Ce(sub x)CuO4 samples with excellent superconducting properties were obtained in thin films and their optical and X-ray photoelectron spectroscopy (XPS) studies were performed with regard to the Ce content and reducing treatment. Substituted BiSr-Ln-Cu-O thin films were prepared and growth conditions for Bi-system with 2-2-1-2 and 2-2-2-2 phases were found. Moreover, a new 2-2-1-2 phase in the simple Bi-Sr-Cu-O system was fabricated by thin film processing and 80 K superconductivity was obtained.