Polyimides containing pendent siloxane groups

The incorporation of siloxane units into the backbone of aromatic polyimides has been shown to impart certain advantages over the unmodified polyimides. These include enhanced solubility, lower moisture adsorption, lower dielectric constant, improved toughness and surface modification. Also, when exposed to an atomic oxygen environment these materials form an in-situ silicate (SiO2) surface coating which protects the underlying material from further erosion. These unique advantages make polyimide-siloxanes useful in a variety of electronic and aerospace applications. As part of an effort on high performance polymeric materials for potential aerospace applications, polyimides containing pendent siloxane groups are under study. These materials were prepared by reacting a functionalized siloxane compound with polyimides containing benzhydrol groups. Thin films of the polymers exhibited glass transition temperatures ranging from 167 to 235 C. Tensile strengths and moduli measured at 23 C ranged from 11 to 14 ksi and 250 to 450 ksi, respectively. The dielectric constant was lowered substantially from that of the unmodified polyimide.