Lubricant evaluation of the alpha and beta joints, phase 2

A research study was conducted to evaluate dry film lubrication of long life space components such as the alpha and beta joints of the Space Station. The problem addressed in the report pertains to the longevity of sputtered MoS2 or ion plated lead films in a rolling contact environment. A special technique was devised for the experiments, which incorporated a coated ball cyclically loaded against a flat plate. At fixed intervals the surface of the coating was photographed at 100X magnification. By computer scanning the photographs, the rate of coating loss was determined. Experimental variables include load and surface finish of the plate. A theory was developed to analyze the state of stress between ball and flat. The stress condition in the ball apparatus was related to the state of stress under rolling contact conditions. Based on the experiments life appeared to decrease with increasing load and increasing surface roughness. An ion plated lead film gave better life than a sputtered MoS2 film. However, by keeping the interfacial shear stress at a low level, adequate coating life was achieved for either coating. For the lead film, the critical stress was about 0.19 GPa (28 ksi). The study dealt only with mechanical wear. Before a coating is selected for a critical space application, other factors such as reaction with atomic oxygen must also be considered.