Long cycle life rechargeable lithium batteries

Cycle life and safety of delta-LiAl/TiS2 cells were evaluated using laboratory and AA-size cells. Analysis of the alloys (which contained 60, 70, 80, or 85 wt-pct. lithium and are designated 60 LiAl etc.) showed them to contain a mixture of elemental Li and Al4Li9. Cycling efficiencies correlated with the amount of free lithium in the anode. Using an electrolyte with the composition 48 v/o THF:48 v/o 2-MeTHF:4 v/o 2-MeF/LiAsF6(1.5M), a 70 LiAl/TiS2 laboratory cell yielded a cycling efficiency of 96.4 pct. when cycled at a 100 pct. discharge depth which compares well with Li anode cycling efficiencies of 96 to 97.5 pct. obtained previously in this electrolyte. The highest cycling efficiency of any delta-LiAl/TiS2 laboratory cell was 96.7 pct. when the 60 LiAl alloy was used with the 35 v/o PC:35 v/o EC:30 v/o triglyme/LiAsF6(1.0M) electrolyte. The 70 LiAl alloy was selected for further testing in AA cells since it was malleable for the fabrication of spirally wound electrodes, and its overall cycling performance was sufficiently good. AA-size 70 LiAl/TiS2 cells appear to have capacity/rate properties similar to those for identical Li/TiS2 cells. The use of the delta-LiAl alloy anodes does not appear to offer any safety advantage when cycled cells are shorted or heated.