The effects of long-duration space exposure on the mechanical properties of some carbon-reinforced resin matrix composites

Long Duration Exposure Facility (LDEF) Experiment A0175 involved the non-instrumented exposure of seven carbon-fiber reinforced resin-matrix advanced composite panels contained in two trays - A7 and A1. These two trays were located, respectively, on the leading and trailing faces of LDEF, obliquely oriented to the RAM (Row 9) and WAKE (Row 3) directions. The identity and location of the seven panels, which consisted of six flat laminates of the following material systems are shown: carbon/epoxy (T300/934), carbon/bismaleimide (T300/F178), and carbon/polyimide (C6000/LARC-160 and C6000/PMR-15), plus one bonded honeycomb sandwich panel (T300/934 face sheets and Nomex core) patterned after the Space Shuttle payload bay door construction. These material systems were selected to represent a range of then-available matrix resins which, by virtue of their differing polymer chemistry, could conceivably exhibit differing susceptibility to the low-earth orbit (LEO) environment. The principal exposure conditions of the LDEF environment at these tray locations are shown. Noteworthy to some of the observations discussed is the four-orders-of magnitude difference in the atomic oxygen (AO) fluence, which made a shallow incidence angle (approximately 22 deg) to Tray A7, while Tray A1 on the trailing face was essentially shielded from AO exposure. This evaluation focused on determining the individual and relative suitability of a variety of resin-matrix composite systems for long-term space structural applications. This was accomplished primarily by measuring and comparing a range of engineering mechanical properties on over 300 test coupons sectioned from the flight panels and from identical control panels, and tested at ambient and elevated temperatures. This testing was supported by limited physical characterization, involving visual examination of flight panel surface features, measurements of weight loss and warpage, and examination for changes in internal integrity (micro cracking, delamination) by ultrasonic c-scan and polished cross-sections.