Kinetic Study of Mass Transfer by Sodium Hydroxide in Nickel Under Free-convection Conditions /by Don R. Mosher and Robert A. Lad

An investigation was conducted using static capsules fabricated from "L" nickel tubing to determine the effect of temperature level, temperature gradient, and test duration on corrosion and mass transfer by molten sodium hydroxide under free-convection conditions. A base temperature range from 1000 degrees to 1600 degrees F with temperature differences to 500 degrees was studied. The rate of mass transfer was found to be strongly dependent on both temperature level and gradient. The rate shows little tendency to decrease for test durations up to 200 hours, although the concentration of nickel in the melt approaches a limited value after 100 hours.