Optimum design of a composite structure with ply-interleaving constraints

The application of composite materials to aircraft construction has provided the designer with increased flexibility. The orientation of plies can be tailored to provide additional aeroelastic performance unobtainable with an isotropic material. A tailored laminate is made up of plies of several orientations, usually 0 deg, 45 deg, -45 deg, and 90 deg. The direction of the 0 deg plies, does not need to be oriented with the leading edge, but can be varied to obtain a wide variety of structural properties. Also, the number of plies of each orientation varies from one zone to another on the planform. Thus, a thick laminate with mainly 0 deg plies may form the root zone, and a thinner laminate with mainly +45 deg plies may form the leading edge zone. Tailored laminates were designed using complicated optimization programs. Unfortunately, many tailored designs must be modified before they are manufactured. The modification adds weight and decreases performance. One type of modification is ply interleaving, an overlap of plies between zones on the laminate. These interleaves are added to ensure that zones with varying ply percentages can be connected without loss of strength. In this paper, the constraints needed to eliminate interleaves in the laminate optimization process will be described and implemented in a structural optimization problem. The method used has the potential to prevent changes to composite laminates late in the design cycle.